Silver Conductive Paste

for Automotive Glass Applications

We offer a silver paste formulated for car defogging. It is non-toxic and lead free paste. Screen-printable silver paste on advanced silver spherical powder and mono dispersed technology. It is suitable and good matching with auto glass rear window.Our silver paste is compatible with auto glass, super excellent conductivity, excellent printing properties, showing good adhesion and chemical resistance.

Precious Metal Pastes

These are thick, viscous formulations that contain finely divided precious metal particles dispersed in a carrier medium.

They are commonly used in the electronics industry for applications such as printed circuit boards, solar cells, and thick film resistors.

The pastes are screen-printed onto substrates and then fired at high temperatures to form conductive traces or resistive elements.

More

  Our Silver Paste Properties

  • Lead and cadmium free system
  • Odorless
  • Super excellent conductivity with system capability for a wide range of resistivity
  • Excellent fired density giving good hiding power to clips soldered on to silver fired directory on glass and silicon wafer
  • Long screen life
  • Robust printing performance
  • Thixotropic modified and Fully blend able system

SLTX10 is a Silver Paste Formulated for Automotive Glass Applications

High temperature sintered conductive silver paste, For soda lime glass, float glass surface glazing; Sintering temperature is wide,after sintering, the adhesion is excellent, the surface is fine, the welding performance is excellent, the electric conductivity is stable, the weather resistance is excellent.

SLTX10 to make available surface of the fired silver to achieved good solder wetting without burnishing.

Typical properties

Silver Paste For Tempered Glass:


Product Code

SLT5010
SLT6010
SLT7010
SLT8010
SLT8810
Silver Content
50±1
60±1
70±1
80±1
88±1
Solid Content
51-55
61-65
71-78
81-85
89-92
Odor
Odorless
Color
Grey To Creamy
Fineness
≤ 20 μm
Viscosity
35±10 Pa.s
40±10 Pa.s
75±15 Pa.s
100±15 Pa.s
120±20 Pa.s
Electrical Resistivity (20 μm)
≤ 22 MOPS
≤ 16 MOPS
≤ 9 MOPS
≤ 4 MOPS
≤ 3 MOPS
Adhesion
No Material Removal
Screen Type
250-325 mesh
Drying Condition
3-5 min @ 150-180 °C
Sintering Condition
3-5 min @ 650-720 °C Box Oven
Film Thickness After sintering
5-7 μm
6-8 μm
7-9 μm
8-10 μm
10-12 μm
Thinner
SSPX10
Shelf Life
12 Month in 5-10 °C Dry Area
Durability
Chemical resistance alkaline and acid attacks
Mechanical resistance against abrasion
Stability (Thixotropic Modified)
Before use stir very well , use paste at room temperature
Pull Strength After Sintering
150 N/cm2

Safety
Safety protection is necessary when using the production
Careful not to touch eyes
If it gets,should rinse with water and consult doctor as soon as possible

Silver Paste For Laminated Glass:


Product Code

SLA80
Silver Content
80±1
Solid Content
81-85
Odor
Odorless
Color
Grey To Creamy
Fineness
≤ 20 μm
Viscosity
100±15 Pa.s
Electrical Resistivity (20 μm)
≤ 4 MOPS
Adhesion
No Material Removal
Screen Type
250-325 mesh
Drying Condition
3-5 min @ 150-180 °C
Sintering Condition
3-5 min @ 600-680 °C Box Oven
Film Thickness After sintering
8-10 μm
Thinner
SSPX10
Shelf Life
12 Month in 5-10 °C Dry Area
Durability
Chemical resistance alkaline and acid attacks
Mechanical resistance against abrasion
Stability (Thixotropic Modified)
Before use stir very well , use paste at room temperature
Pull Strength After Sintering
150 N/cm2

Safety
Safety protection is necessary when using the production
Careful not to touch eyes
If it gets,should rinse with water and consult doctor as soon as possible

Advantages OF OUR CONDUCTIVE SILVER PASTE

Excellent Printability, Conductivity And Adhesion Strength

Pb, Hg, Cd, And Phetalate Free RoHS Compliang

Excellent Weather Resistance And Chemical Stability

The Resistance Value Can Be Adjusted Arbitrarily With The Same Series Of Silver Pastes

Contact our team of experts to discuss your specific needs and discover how we can help you unlock the full potential of these valuable resources while upholding the principles of sustainability.